Boron substitution in silicate bioactive glass scaffolds to enhance bone differentiation and regeneration

Agata Szczodra, Amel Houaoui, Rémy Agniel, Ludovic Sicard, Susanna Miettinen, Jonathan Massera, Caroline Gorin

Research output: Contribution to journalArticleScientificpeer-review

Abstract

Commercially available bioactive glasses (BAGs) are exclusively used in powder form, due to their tendency to crystallize. Silicate BAG 1393 was developed to allow fiber drawing and scaffold sintering, but its slow degradation limits its potential. To enable scaffold manufacturing while maintaining glass dissolution rate close to that of commercially available BAGs, the borosilicate glass 1393B20 was developed. This study investigates the potential of 1393B20 scaffolds to support bone regeneration and mineralization in vitro and in vivo, in comparison to silicate 1393. Both scaffolds supported human adipose stem cells proliferation, either in direct contact for the 1393, or mainly around for the 1393B20. Similarly, both BAGs induced osteogenesis and angiogenesis in vitro, with a better pro-angiogenic influence of the 1393B20. In addition, these scaffolds supported bone regeneration and osteoclast/osteoblast activity in vivo in critical-sized rat calvarial defect. Nevertheless, mineralization and collagen formation were significantly enhanced for the 1393B20, at 3-months post-implantation, assigned to faster and more complete dissolution of the scaffolds. Thus, 1393B20 demonstrates greater promise for bone tissue engineering certainly due to its time-controlled release of boron and silicon. Statement of significance: Bioactive glasses (BAGs) show great promise in bone tissue engineering as they effectively bond with bone tissue, fostering integration and regeneration. Silicate BAG 1393 was developed to allow fiber drawing and scaffold sintering, but its slow degradation limits its potential. To enable scaffold manufacturing while maintaining glass dissolution rate close to that of commercially available BAGs, the borosilicate glass 1393B20 was developed. Both BAGs induced osteogenesis and angiogenesis in vitro, with a better pro-angiogenic influence of the 1393B20. The presence of boron in the 1393B20 enhanced mineralization and collagen formation in vivo compared to 1393, probably due to its faster dissolution rate. Here, 1393B20 demonstrated greater promise for bone tissue engineering compared to the well-known 1393 BAG.

Original languageEnglish
JournalActa Biomaterialia
DOIs
Publication statusE-pub ahead of print - 2024
Publication typeA1 Journal article-refereed

Keywords

  • 3D-printed scaffolds
  • Bone regeneration
  • Bone tissue engineering
  • Boron
  • Calvarial bone defect

Publication forum classification

  • Publication forum level 2

ASJC Scopus subject areas

  • Biotechnology
  • Biomaterials
  • Biochemistry
  • Biomedical Engineering
  • Molecular Biology

Fingerprint

Dive into the research topics of 'Boron substitution in silicate bioactive glass scaffolds to enhance bone differentiation and regeneration'. Together they form a unique fingerprint.

Cite this