Characteristics of carbide-free medium-carbon bainitic steels in high-stress abrasive wear conditions

Oskari Haiko, Pentti Kaikkonen, Mahesh Somani, Kati Valtonen, Jukka Kömi

Research output: Contribution to journalArticleScientificpeer-review

2 Downloads (Pure)


This study encompasses a comprehensive account of the abrasive wear properties of carbide-free, ultrahigh-strength bainitic steels processed through ausforming at three different temperatures well below the recrystallization stop temperature followed by bainitic transformation at temperatures close to the Ms temperature. Five medium-carbon, high-silicon compositions were designed for the study by suitably varying the alloying levels of carbon, vanadium, niobium, molybdenum, and aluminum. While ausforming at lower temperatures enabled a large number of nucleation sites leading to significant refinement of bainitic laths, the decomposition of austenite at relatively low transformation temperatures was accelerated due to the presence of a high dislocation density, thus enabling completion of bainitic transformation in a reasonable length of time. The steels were characterized in respect of microstructural features and mechanical properties, besides evaluation of wear resistance through a high-stress abrasive wear testing method with natural granite abrasives. The microstructures comprised different fractions of bainitic ferrite and/or granular bainite (56–68%), martensite (0–25%), besides a significant fraction of retained austenite (20–34%) manifesting as pools and also interlath films, depending on the ausforming conditions and subsequent cooling paths. A tensile strength of 1900 MPa level was achieved with hardness exceeding 500 HV for the medium-temperature ausformed steel containing a high carbon content that also showed lowest mass loss in the wear test. The hardness-to-mass loss ratio appeared highly promising with some of the carbide-free bainitic steels on par with or better than the reference martensitic steel. The high work-hardening capability as a consequence of the strain-induced austenite to martensite transformation was considered as the main factor for the superior abrasive wear resistance of the carbide-free bainitic steels.

Original languageEnglish
Article number203386
Number of pages12
Publication statusPublished - 15 Sept 2020
Publication typeA1 Journal article-refereed


  • Abrasion
  • Bainite
  • Microstructure
  • Steel
  • Wear testing

Publication forum classification

  • Publication forum level 2

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry


Dive into the research topics of 'Characteristics of carbide-free medium-carbon bainitic steels in high-stress abrasive wear conditions'. Together they form a unique fingerprint.

Cite this