Chemically tailored dielectric-to-metal transition for the design of metamaterials from nanoimprinted colloidal nanocrystals

Aaron T. Fafarman, Sung Hoon Hong, Humeyra Caglayan, Xingchen Ye, Benjamin T. Diroll, Taejong Paik, Nader Engheta, Christopher B. Murray, Cherie R. Kagan

Tutkimustuotos: ArtikkeliScientificvertaisarvioitu

66 Sitaatiot (Scopus)

Abstrakti

We demonstrate optical metamaterial design using colloidal gold nanocrystal building blocks. In the solid state, chemically exchanging the nanocrystals' surface-capping molecules provides a tailorable dielectric-to-metal transition exhibiting a 1010 range in DC conductivity and dielectric permittivity ranging from everywhere positive to everywhere negative throughout the visible-to-near-IR. Direct, wide-area nanoimprinting of subwavelength superstructures at room temperature, on plastic and glass substrates, affords plasmonic resonances ranging from 660 to 1070 nm, in agreement with numerical simulations.

AlkuperäiskieliEnglanti
Sivut350-357
Sivumäärä8
JulkaisuNano Letters
Vuosikerta13
Numero2
DOI - pysyväislinkit
TilaJulkaistu - 13 helmik. 2013
Julkaistu ulkoisestiKyllä
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

!!ASJC Scopus subject areas

  • Bioengineering
  • Yleinen kemia
  • Yleinen materiaalitiede
  • Condensed Matter Physics
  • Mechanical Engineering

Sormenjälki

Sukella tutkimusaiheisiin 'Chemically tailored dielectric-to-metal transition for the design of metamaterials from nanoimprinted colloidal nanocrystals'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä