Effect of Environment on Bromobutyl Rubber–Steel Adhesion

Essi Sarlin, Ari Rosling, Mari Honkanen, Mari Lindgren, Mira Juutilainen, Minna Poikelispää, Paavo Laihonen, Minnamari Vippola, Jyrki Vuorinen

Tutkimustuotos: ArtikkeliScientificvertaisarvioitu

3 Sitaatiot (Scopus)

Abstrakti

Optimizing the maintenance cycles of rubber-lined components is of great importance. Especially for the industry sectors operating under demanding conditions, challenges in the lifetime evaluation of rubber linings may cause apparent premature failures. Thus, understanding the effect of environmental factors on the performance and durability of rubber linings, as well as on the weakest links of the structure in certain environments, is essential. The performances of bromobutyl rubber and rubber–steel interfaces after exposure to different environments, namely, high temperature (95 8C), moisture (95% relative humidity and immersion), and sulfuric acid (solution with 75 g/L of acid) were investigated. The weakest link of the rubber–metal structure and, consequently, the location of the fracture were mostly within the adhesive layer or at the primer–metal interface. However, the most degraded component of the adhesive system depends on the aging environments.

AlkuperäiskieliEnglanti
Sivut429-444
Sivumäärä16
JulkaisuRubber Chemistry and Technology
Vuosikerta93
Numero2
DOI - pysyväislinkit
TilaJulkaistu - 2020
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Julkaisufoorumi-taso

  • Jufo-taso 1

!!ASJC Scopus subject areas

  • Polymers and Plastics
  • Materials Chemistry

Sormenjälki

Sukella tutkimusaiheisiin 'Effect of Environment on Bromobutyl Rubber–Steel Adhesion'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä