Effect of post-heat-treatment on the structural, spectroscopic and dissolution properties of a highly stable Er3+-doped multi-component phosphate glass

Diego Pugliese; Alexander Veber; Arnaud Lemière; Nadia G. Boetti; Laeticia Petit

doi:10.1016/j.jallcom.2021.160878

Effect of post-heat-treatment on the structural, spectroscopic and dissolution properties of a highly stable Er³⁺-doped multi-component phosphate glass

Diego Pugliese, Alexander Veber, Arnaud Lemière, Nadia G. Boetti, Laeticia Petit

Fysiikka

Tutkimustuotos: Artikkeli › Tieteellinen › vertaisarvioitu

6 Sitaatiot (Scopus)

12 Lataukset (Pure)

Abstrakti

In this paper, the impact of the post-heat-treatment on the structural and spectroscopic properties as well as on the chemical durability of a thermally stable Er³⁺-doped phosphate glass in the system P₂O₅ - K₂O - Al₂O₃ - B₂O₃ - BaO - PbO - La₂O₃ - Gd₂O₃ is reported. Two crystalline phases, namely La, Gd-monazite and AlKP₂O₇, were found to precipitate from the surface of the glass after heat-treatment, as confirmed by both X-ray Diffraction (XRD) and Scanning Electron Microscopy/Energy Dispersive X-ray (SEM/EDX) analyses. Moreover, the heat-treatment was responsible for the formation of a more polymerized glass network close to the surface crystalline layer as evidenced using micro-Raman spectroscopy. From the changes in the Er³⁺ optical properties, some of the Er³⁺ ions are suspected to enter in the crystals. Both the as-prepared and heat-treated glasses were subjected to a degradation test in hydrochloric acid (HCl) and showed a congruent and incongruent dissolution behavior, respectively.

Alkuperäiskieli	Englanti
Artikkeli	160878
Sivumäärä	7
Julkaisu	Journal of Alloys and Compounds
Vuosikerta	883
DOI - pysyväislinkit	https://doi.org/10.1016/j.jallcom.2021.160878
Tila	Julkaistu - 25 marrask. 2021
OKM-julkaisutyyppi	A1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Julkaisufoorumi-taso

Jufo-taso 1

!!ASJC Scopus subject areas

Mechanics of Materials
Mechanical Engineering
Metals and Alloys
Materials Chemistry

Pääsy asiakirjaan

10.1016/j.jallcom.2021.160878

Effect_of_post_heat_treatment_on_the_structural
CC BY-NC-ND
Accepted author manuscript, 1,27 MBLisenssi: CC BY-NC-ND

https://urn.fi/URN:NBN:fi:tuni-202111098285Lisenssi: CC BY-NC-ND

Tampereen Mikroskopiakeskus
Vippola, M. (Manager), Honkanen, M. (Operator) & Salminen, T. (Operator)
Tekniikan ja luonnontieteiden tiedekunta
Laitteistot/tilat: Facility

Siteeraa tätä

@article{d2caa0fd2da043c6b2e6b395607888a7,

title = "Effect of post-heat-treatment on the structural, spectroscopic and dissolution properties of a highly stable Er3+-doped multi-component phosphate glass",

abstract = "In this paper, the impact of the post-heat-treatment on the structural and spectroscopic properties as well as on the chemical durability of a thermally stable Er3+-doped phosphate glass in the system P2O5 - K2O - Al2O3 - B2O3 - BaO - PbO - La2O3 - Gd2O3 is reported. Two crystalline phases, namely La, Gd-monazite and AlKP2O7, were found to precipitate from the surface of the glass after heat-treatment, as confirmed by both X-ray Diffraction (XRD) and Scanning Electron Microscopy/Energy Dispersive X-ray (SEM/EDX) analyses. Moreover, the heat-treatment was responsible for the formation of a more polymerized glass network close to the surface crystalline layer as evidenced using micro-Raman spectroscopy. From the changes in the Er3+ optical properties, some of the Er3+ ions are suspected to enter in the crystals. Both the as-prepared and heat-treated glasses were subjected to a degradation test in hydrochloric acid (HCl) and showed a congruent and incongruent dissolution behavior, respectively.",

keywords = "Dissolution test, Er luminescence property, Glass-ceramic, Heat-treatment, Nucleation and growth, Phosphate glass",

author = "Diego Pugliese and Alexander Veber and Arnaud Lemi{\`e}re and Boetti, {Nadia G.} and Laeticia Petit",

note = "Funding Information: D.P. acknowledges the Interdepartmental Center “PhotoNext” of Politecnico di Torino for the partial support of this research effort. Academy of Finland Research and Innovation PREIN-320165 and Academy Project - 326418 ) is greatly acknowledged for the financial support. This work made use of Tampere Microscopy Center facilities at Tampere University. Funding Information: D.P. acknowledges the Interdepartmental Center ?PhotoNext? of Politecnico di Torino for the partial support of this research effort. Academy of Finland Research and Innovation PREIN-320165 and Academy Project - 326418) is greatly acknowledged for the financial support. This work made use of Tampere Microscopy Center facilities at Tampere University. Publisher Copyright: {\textcopyright} 2021 Elsevier B.V.",

year = "2021",

month = nov,

day = "25",

doi = "10.1016/j.jallcom.2021.160878",

language = "English",

volume = "883",

journal = "Journal of Alloys and Compounds",

issn = "0925-8388",

publisher = "Elsevier B.V.",

}

TY - JOUR

T1 - Effect of post-heat-treatment on the structural, spectroscopic and dissolution properties of a highly stable Er3+-doped multi-component phosphate glass

AU - Pugliese, Diego

AU - Veber, Alexander

AU - Lemière, Arnaud

AU - Boetti, Nadia G.

AU - Petit, Laeticia

N1 - Funding Information: D.P. acknowledges the Interdepartmental Center “PhotoNext” of Politecnico di Torino for the partial support of this research effort. Academy of Finland Research and Innovation PREIN-320165 and Academy Project - 326418 ) is greatly acknowledged for the financial support. This work made use of Tampere Microscopy Center facilities at Tampere University. Funding Information: D.P. acknowledges the Interdepartmental Center ?PhotoNext? of Politecnico di Torino for the partial support of this research effort. Academy of Finland Research and Innovation PREIN-320165 and Academy Project - 326418) is greatly acknowledged for the financial support. This work made use of Tampere Microscopy Center facilities at Tampere University. Publisher Copyright: © 2021 Elsevier B.V.

PY - 2021/11/25

Y1 - 2021/11/25

N2 - In this paper, the impact of the post-heat-treatment on the structural and spectroscopic properties as well as on the chemical durability of a thermally stable Er3+-doped phosphate glass in the system P2O5 - K2O - Al2O3 - B2O3 - BaO - PbO - La2O3 - Gd2O3 is reported. Two crystalline phases, namely La, Gd-monazite and AlKP2O7, were found to precipitate from the surface of the glass after heat-treatment, as confirmed by both X-ray Diffraction (XRD) and Scanning Electron Microscopy/Energy Dispersive X-ray (SEM/EDX) analyses. Moreover, the heat-treatment was responsible for the formation of a more polymerized glass network close to the surface crystalline layer as evidenced using micro-Raman spectroscopy. From the changes in the Er3+ optical properties, some of the Er3+ ions are suspected to enter in the crystals. Both the as-prepared and heat-treated glasses were subjected to a degradation test in hydrochloric acid (HCl) and showed a congruent and incongruent dissolution behavior, respectively.

AB - In this paper, the impact of the post-heat-treatment on the structural and spectroscopic properties as well as on the chemical durability of a thermally stable Er3+-doped phosphate glass in the system P2O5 - K2O - Al2O3 - B2O3 - BaO - PbO - La2O3 - Gd2O3 is reported. Two crystalline phases, namely La, Gd-monazite and AlKP2O7, were found to precipitate from the surface of the glass after heat-treatment, as confirmed by both X-ray Diffraction (XRD) and Scanning Electron Microscopy/Energy Dispersive X-ray (SEM/EDX) analyses. Moreover, the heat-treatment was responsible for the formation of a more polymerized glass network close to the surface crystalline layer as evidenced using micro-Raman spectroscopy. From the changes in the Er3+ optical properties, some of the Er3+ ions are suspected to enter in the crystals. Both the as-prepared and heat-treated glasses were subjected to a degradation test in hydrochloric acid (HCl) and showed a congruent and incongruent dissolution behavior, respectively.

KW - Dissolution test

KW - Er luminescence property

KW - Glass-ceramic

KW - Heat-treatment

KW - Nucleation and growth

KW - Phosphate glass

U2 - 10.1016/j.jallcom.2021.160878

DO - 10.1016/j.jallcom.2021.160878

M3 - Article

AN - SCOPUS:85108454371

SN - 0925-8388

VL - 883

JO - Journal of Alloys and Compounds

JF - Journal of Alloys and Compounds

M1 - 160878

ER -