Formation of corrosion products on zinc in wet supercritical and subcritical CO2: In-situ spectroscopic study

A. Kaleva, T. Tassaing, V. Saarimaa, G. Le Bourdon, P. Väisänen, A. Markkula, E. Levänen

Tutkimustuotos: ArtikkeliTieteellinenvertaisarvioitu

15 Sitaatiot (Scopus)
13 Lataukset (Pure)

Abstrakti

Formation of corrosion products on zinc was investigated with in-situ Raman and FTIR when exposed to wet supercritical carbon dioxide (scCO2) and subsequent depressurization. Zinc oxide (ZnO) and smithsonite (ZnCO3) formed on zinc in scCO2. The dissolved water precipitated as liquid water in the reaction cell during depressurization. Formation of ZnO, ZnCO3 and a needle-like zinc hydroxy carbonate species on zinc was observed inside a sessile water droplet during conditions simulating the depressurization phase. Addition of oxygen accelerated the formation of the carbonate species due to higher cathodic activity that increased zinc dissolution.

AlkuperäiskieliEnglanti
Sivumäärä10
JulkaisuCorrosion Science
Vuosikerta174
DOI - pysyväislinkit
TilaJulkaistu - 1 syysk. 2020
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Julkaisufoorumi-taso

  • Jufo-taso 3

!!ASJC Scopus subject areas

  • Yleinen kemia
  • Yleinen kemian tekniikka
  • Yleinen materiaalitiede

Sormenjälki

Sukella tutkimusaiheisiin 'Formation of corrosion products on zinc in wet supercritical and subcritical CO2: In-situ spectroscopic study'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä